纳米SiC颗粒增强2024铝基复合材料的力学性能研究  

Mechanical Properties of Nano-SiC_p Reinforced 2024 Aluminum Composite

作　　者：田晓风[1] 肖伯律[1] 樊建中[1] 万志永[1] 左涛[1] 张维玉[1] 

机构地区：[1]北京有色金属研究总院国家有色金属复合材料工程技术研究中心,北京100088

出　　处：《稀有金属》2005年第4期521-525,共5页Chinese Journal of Rare Metals

基　　金：国家863计划资助项目(2002AA302502)

摘　　要：采用粉末冶金法制备了1%(体积分数)纳米SiC颗粒增强2024铝基复合材料,并研究了其力学性能。实验结果表明,1%纳米SiC颗粒增强2024铝基复合材料具有优良的室温力学性能,并且在200℃时表现了较好的高温性能,在315℃时强度下降。研究表明,纳米SiC可以增加增强粒子的表面积,减小增强粒子的颗粒间距,使大量弥散分布的纳米SiC颗粒起到钉扎位错的作用,而且可以细化2024铝基体的晶粒,因而表现了良好的力学性能。The study of mechanical properties of 1% nano-SiC_p reinforced 2024 aluminum composite fabricated by powder metallurgy method was undertaken. The results show that 1% nano-SiC_p/2024 has excellent tensile properties at room temperature and 200 ℃, especially having good yield stress, however its tensile strength decrease largely at 315 ℃. These results reveal that nano-SiC_p particles can increase the surface area of interface between nano-SiC_p and base, and reduce the space between nano-SiC_p particles. Th...

关 键 词：纳米SIC颗粒 复合材料 粉末冶金 