聚苯乙烯-甲基丙烯酸甲酯接枝共聚物的合成  

Synthesis of graft copolymer of poly(styrene-g-methylmethacrylate)

作　　者：张永明[1] 罗宁[1] 余海霞[1] 应圣康[1] 

机构地区：[1]华东理工大学活性聚合实验室

出　　处：《合成橡胶工业》1999年第2期19-22,共4页China Synthetic Rubber Industry

基　　金：国家自然科学基金;上海市教委曙光计划研究课题

摘　　要：通过氯甲基化反应在线型聚苯乙烯（ＰＳ）的苯环上定量地引入氯甲基（—ＣＨ２Ｃｌ），合成了氯甲基化聚苯乙烯大分子引发剂ＰＳ—ＣＨ２Ｃｌ，在氯化亚铜／α，α′－联二吡啶配合物（ＣｕＣｌ／ｂｐｙ）催化下，以ＰＳ—ＣＨ２Ｃｌ引发甲基丙烯酸甲酯（ＭＭＡ）聚合，合成了聚苯乙烯－甲基丙烯酸甲酯接枝共聚物。用红外光谱和核磁共振氢谱证实了接枝共聚物的结构，测定了接枝共聚物中ＰＭＭＡ支链数目、接枝共聚物的支链长度、接枝率及接枝效率。结果表明，用这种方法制备的接枝共聚物相对分子质量分布较窄，接枝率可控，接枝效率高达９２％～９８％。A series of graft copolymer of poly(styrene-g-methylmethacrylate)were prepared.The graft polymerization of methylmethacrylate was carried out in xylene solution with PS CH2Cl as macroinitiator,which was prepared with linear PS chloromethylated by chloromethyl ether.The graft copolymer of poly(styrene-g-methylmethacrylate)was confirmed by IR,1H-NMR spectra after purification.The numbers of the branches on PS chains,the length of the branches,the graft ratio and the graft efficiency were also investigated.Th...

关 键 词：聚苯乙烯 甲基丙烯酸甲酯 接枝共聚物 接枝率 接枝效率 

分 类 号：TQ325.2[化学工程—合成树脂塑料工业]