烧结助剂对B_4C/B-Al烧结性能的影响  

Influence of Sintering Aids on Sintering Performance of B_4C/B-Al

作　　者：王东山[1] 薛向欣[1] 

机构地区：[1]东北大学材料与冶金学院辽宁省高校硼资源生态化综合利用技术与硼材料重点试验室辽宁省硼资源综合开发利用工程技术研究中心,辽宁沈阳110004

出　　处：《稀有金属与硬质合金》2008年第1期20-23,50,共5页Rare Metals and Cemented Carbides

摘　　要：在1 850℃、恒温1.5 h、真空碳管炉氩气保护条件下研究了烧结助剂Al2O3-Y2O3对B4C/B-Al复合材料烧结性能的影响。研究表明:Al2O3-Y2O3的加入能有效改善B4C/B-Al复合材料的物理力学性能,与未加入烧结助剂试样相比,其体积密度平均提高26.94%,气孔率平均降低32.1%,抗压强度平均提高85.81%。同时指出,在本试验条件下加入单质B、Al发生原位反应生成硼铝化合物并不能促进B4C材料的烧结,而且随着B、Al含量的增加,B4C材料的力学性能逐渐降低。The influences of sintering aids Al2O3-Y2O3on sintering performance of B4C/B-Al composites were studied in vacuum carbon tube furnace under argon atmosphere at 1 850 ℃ holding 1.5 h.The results indicated that physical mechanical properties of B4C/B-Al composites are improved through adding Al2O3-Y2O3.Comparing to samples without sintering aids the volume density of the samples increase 26.94%,porosity decreases 32.1%,and compression increases 85.81% averagely.At the same time it was pointed out that the sin...

关 键 词：烧结助剂 硼铝化合物 B4C 烧结性能 力学性能 

分 类 号：TQ174[化学工程—陶瓷工业]