Synthesis and Luminescence Properties of Red Phosphors:Mn^(2+) Doped MgSiO_3 and Mg_2SiO_4 Prepared by Sol-Gel Method  

作　　者：林林 尹民 施朝淑 张慰萍 游宝贵 

机构地区：[1]Structure Research Laboratory,University of Science and Technology of China,Chinese Academy of Sciences [2]Physics Department,University of Science and Technology of China,Hefei 230026,China [3]Physics Department,University of Science and Technology of China

出　　处：《Journal of Rare Earths》2006年第z2期104-107,共4页稀土学报（英文版）

基　　金：Project is supported by National High Technology Research and Development Program of China (863 Program) (2002 AA 324060);National Natural Science Foundation of China (10404028)

摘　　要：Sol-gel method was utilized to synthesize two different series of red silicate phosphors : MgSiO3 and Mg2SiO4 powder samples doped with Mn2+, conducted the investigation of red long-lasting phosphor: MgSiO3 : Eu2 + , Dy3+, Mn2+ . TGA curves of the gel precursor for two series depicted that the loss of residual organic groups and NO3 groups occurs below 450℃. According to the XRD patterns, the major diffraction peaks of the MgSiO3 and Mg2SiO4 series are consistent with a proto-enstatite structure (JCPDS No.11-0273) and a forsterite structure (JCPDS No.85-1364) respectively. With the excitation at 415 nm, the red emission band of Mn2+ ions is peaked at 661 nm for MgSiO3:1%(atom fraction) Mn2+ or 644 nm for MgiSiO4: 1 %(atom fraction) Mn2+ . Compared with Mg2SiO4:Mn2+ samples, MgSiO3:Mn2+ samples exhibit higher luminescence intensity and higher quenching concentration. In addition, the two series co-doped with Eu2+ , Dy3+ , Mn2+ were also prepared. Photo-luminescence and afterglow properties of the two co-doped series were analyzed, which show that MgSiO3: Eu2 + , Dy3+ , Mn2+ is more suitable for a red long-lasting phosphor.Sol-gel method was utilized to synthesize two different series of red silicate phosphors : MgSiO3 and Mg2SiO4 powder samples doped with Mn2+, conducted the investigation of red long-lasting phosphor: MgSiO3 : Eu2 + , Dy3+, Mn2+ . TGA curves of the gel precursor for two series depicted that the loss of residual organic groups and NO3 groups occurs below 450℃. According to the XRD patterns, the major diffraction peaks of the MgSiO3 and Mg2SiO4 series are consistent with a proto-enstatite structure (JCPDS No.11-0273) and a forsterite structure (JCPDS No.85-1364) respectively. With the excitation at 415 nm, the red emission band of Mn2+ ions is peaked at 661 nm for MgSiO3:1%(atom fraction) Mn2+ or 644 nm for MgiSiO4: 1 %(atom fraction) Mn2+ . Compared with Mg2SiO4:Mn2+ samples, MgSiO3:Mn2+ samples exhibit higher luminescence intensity and higher quenching concentration. In addition, the two series co-doped with Eu2+ , Dy3+ , Mn2+ were also prepared. Photo-luminescence and afterglow properties of the two co-doped series were analyzed, which show that MgSiO3: Eu2 + , Dy3+ , Mn2+ is more suitable for a red long-lasting phosphor.

关 键 词：MANGANESE magnesium silicate ORTHOSILICATE red long-lasting phosphor rare earths 

分 类 号：O482.3[理学—固体物理]