Surface nanostructures in commercial pure Ti induced by high energy shot peening  

作　　者：CHEN Chun-huan REN Rui-ming ZHAO Xiu-juan ZHANG Yu-jun 

机构地区：[1]School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, China School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, China School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, China School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, China

出　　处：《中国有色金属学会会刊：英文版》2004年第z1期215-218,共4页Transactions of Nonferrous Metals Society of China

基　　金：Project(50171017) supported by the National Natural Science Foundation of China; Project(2001101054) supported by Science and Technology Foundation of Liaoning Province

摘　　要：The high-energy shot peening (HESP) technique was used to obtain the surface nanocrystalline microstructure for a hcp metal titanium. XRD, SEM and TEM were applied to characterize the microstructure of the surface layer. Large amount of the deformation twins in the surface layer were observed by SEM in the specimens after HESP treatment in a shot-time, and the number of deformation twins both in a single plane and in intersecting planes increases with HESP time, until the twin character disappears completely in the top surface layer, which means that the severe plastic deformation(SPD) occurs on the surface. The XRD analysis results show that after HESP treatmen for 30 - 60 min the surface grain size decreases to nanoscale. According to the TEM images and corresponding diffraction patterns from SPD areas of the 120 min-treatment specimen, the measured grain size near the surface is about 20 - 30 nm. The grain size in deformation layer increases with the depth from the surface, and the nanostructured layer is about 20 μm in depth. Therefore, the surface nanocrystalline and a gradient microstructure from the surface to the matrix are obtained, which results in the micro-hardness decreasing from surface to the matrix gradually.

关 键 词：SURFACE NANOCRYSTALLIZATION shot PEENING COMMERCIAL PURE TI 

分 类 号：TG174[金属学及工艺—金属表面处理]