Properties and Preparation of Diecasting TiC/AlSi9Cu 1.4 Mg 0.5 Composite

作　　者：杨滨[1] 张济山[2] 陈国香[3] 

机构地区：[1]北京科技大学新金属材料国家重点实验室,北京市学院路30号100083 [2]北京科技大学 [3]南昌大学,100083

出　　处：《特种铸造及有色合金》2002年第S1期101-102,104,共3页Special Casting & Nonferrous Alloys

基　　金：国家自然科学基金资助项目 (597740 32 );江西省自然科学基金资助项目 (9750 1 8)

摘　　要：利用熔铸 -原位反应和压铸成形技术制备了TiC/AlSi9Cu1.4Mg0 .5复合材料 ,测试了复合材料的力学性能。结果表明 :TiC/AlSi9Cu1.4Mg0 .5复合材料的室温抗拉强度为 3 5 4MPa ,比基体合金提高 2 6% ;2 60℃时复合材料的抗拉强度为2 72MPa ,比基体合金提高 46%。复合材料的伸长率与AlSi9Cu1.4Mg0 .The die casting TiC/AlSi9Cu1.4Mg0.5 composite has been prepared successfully by both smelting in situ reaction and die casting technique. The mechanical properties of the composites were measured. The results showed that the ultimate tensile strength of the die casting TiC/AlSi9Cu1.4Mg0.5 composites with 354 MPa at room temperature and 272 MPa at 260 ℃, are higher by 26% and 46% than those of the matrix alloy(280 MPa and 186 MPa)respectively. The elongation of the die casting composite at room temperatur...

关 键 词：原位反应 压铸 铝基复合材料 力学性能 

分 类 号：TB33[一般工业技术—材料科学与工程]