炉料级配对锰硅合金生产的影响  

Charging Mechanism of Coke and Ore Particulates in Production of Manganese-Silicon Alloy

作　　者：翟丹[1] 储少军[1] 张志敏[1] 

机构地区：[1]北京科技大学冶金与生态工程学院,北京100083

出　　处：《过程工程学报》2008年第S1期298-301,共4页The Chinese Journal of Process Engineering

基　　金：国家自然科学基金(编号:50274013)

摘　　要：锰硅合金炉料级配的实验结果表明,2种非均一粒度焦炭混合后的电阻随小焦粒体积比的增加呈非线性变化,当小焦粒的体积占总体积的50%～60%时,混合焦炭的电阻值达到较大值;通过改变矿石的粒度调整混合炉料粒度时,混合炉料的电阻随混合炉料粒度的增加线性减小;透气性随炉料平均粒度增加呈非线性变化,总趋势是减小的.应用实验结果,将6.3MW矿热炉入炉的大、小焦粒体积比由3:2改为5:6,锰矿粒度由80mm破碎为40mm左右时,增大了炉料的电阻,同时炉料的透气性也得到了明显的改善.The effect of particle ration of charging stock for production of ferromanganese-silicon alloy on its properties of resistance and permeability was studied in this work.The experimental results showed that the resistance of two nonuniform granularity mixed cokes varied non-linearly with the size increasing and reached to a larger value,when the volumetric fraction of small particle size of coke was 50%～60%.The resistance of charging stock decreased and the permeability varied non-linearly with increasing of...

关 键 词：硅锰合金 炉料级配 电阻 透气性 

分 类 号：TF792[冶金工程—钢铁冶金]