硫铝酸钙改性硅酸盐水泥性能研究  

Study on properties of Portland cement modified with calcium sulphoaluminate

作　　者：王昕[1] 颜碧兰[1] 刘晨[1] 邓克平[2] 李树清[2] 江丽珍[1] 

机构地区：[1]中国建筑材料科学研究总院,北京100024 [2]金山特种水泥有限公司,内蒙古呼和浩特010080

出　　处：《水泥》2008年第12期1-8,共8页Cement

摘　　要：研究了不同混合材种类及掺量的改性硅酸盐水泥(即阿利特硫铝酸盐水泥)性能变化,以及水泥细度、石膏掺量等对水泥性能的影响,并借助XRD等测试技术对其机理进行探讨。试验结果表明,引入无水硫铝酸钙矿物有利于提高水泥强度,且水泥表现出微膨胀性。随着水泥中混合材掺量的增大,早期强度有所降低,但水泥胶砂流变性和外加剂适应性等有所改善,且混合材种类和品质不同,其作用效果存在较大差异;水泥细度增加,有利于提高早期强度;石膏掺量对水泥性能有严重影响,应进行严格控制。The property change of modified Portland cement(alite sulphate aluminium cement) mixed with different type and content of admixture were studied,and also the effect of fineness and content of gypsum on cement properties as well,The mechanism of these changes was discussed by means of XRD analysis.The results showed that anhydrous calcium sulphoaluminate was helpful to enhance cement strength,and introduce a little expansibility.Increasing the amount of admixture in cement,the early strength decreased,but th...

关 键 词：硫铝酸钙 改性硅酸盐水泥 水泥性能 石膏掺量 混合材 细度 

分 类 号：TQ172.12[化学工程—水泥工业]