绝缘片在粉末工艺合成人造金刚石中的试验研究  

Experimental Research on Insulating Flat for Diamond Synthesis by Powder Catalyst Method

作　　者：李丹[1] 孟继承[1] 张景鑫[1] 朱凤福[1] 周连科[1] 

机构地区：[1]中材高新材料股份有限公司,北京100018

出　　处：《人工晶体学报》2009年第1期175-178,共4页Journal of Synthetic Crystals

摘　　要：本文介绍了一种用氧化铝陶瓷基片制作的绝缘片,应用在粉末工艺合成人造金刚石中。通过在六面顶压机上进行人造金刚石高温、超高压合成的对比实验,结果表明:绝缘片能有效地改善合成腔体内部的温度分布差异,为金刚石的成核生长提供良好的环境。具有绝缘片的粉末合成块在粉末合成工艺中较没有绝缘片粉末合成块合成工艺更稳定。同时由于合成腔体的温场均匀,合成的金刚石颜色、透明度、单产都有很大提高。为进一步提高金刚石的品位进行了实验摸索。This paper introduces a substrate produced by alumina ceramic insulation flat applied to synthesize diamond by powder catalyst method.By comparing experiments on the cubic press in the high-temperature and high-pressure(HTHP)synthesis.The experimental result shows that insulating flat can effectively promote the temperature distribution of the internal cavity,and provide a good environment for the nucleation of diamond.More stable powder synthesis processing has been given by use of insulation flat in the c...

关 键 词：绝缘片 合成腔体 粉末触媒 人造金刚石 

分 类 号：TQ164[化学工程—高温制品工业]