工艺参数对钛/瓷界面组织及性能的影响  

Effects of technology parameters on microstructure and mechanical properties at the interface between porcelain and titanium

作　　者：段珍珍[1] 孙大千[1] 朱松[2] 殷世强[1] 邱小明[1] 

机构地区：[1]吉林大学材料科学与工程学院,长春130022 [2]吉林大学口腔医学院,长春130041

出　　处：《吉林大学学报（工学版）》2009年第1期66-71,共6页Journal of Jilin University:Engineering and Technology Edition

基　　金：吉林省科技发展计划项目(20050511)

摘　　要：应用扫描电镜、能谱、X射线衍射及电子拉伸试验机对钛/瓷界面的微观组织和力学性能进行了研究。结果表明,钛/瓷界面由钛表面氧化膜层和瓷与氧化膜层作用形成的反应层组成,烤瓷工艺参数直接影响钛/瓷界面结构、结合强度和断裂位置。烤瓷温度对钛/瓷界面结合强度影响较大,烤瓷温度为800℃、烤瓷时间为1 min时,钛/瓷界面三点弯曲结合强度为24.7MPa。随着烤瓷温度的提高和烤瓷时间的延长,钛表面氧化膜层和反应层变宽,最终影响钛/瓷界面的结合强度。The microstructure and mechanical properties at the interface between porcelain and titanium were studied using SEM,EDS,XRD and electron tensile testing machine.The results show that the interface between porcelain and titanium is composed of oxide layer formed on titanium and reaction zone between oxide layer and porcelain,the technology parameters have great effects on the microstructure of interface,the bonding strength and fracture position.Among them,the firing temperature demonstrates great effect on ...

关 键 词：材料合成与加工工艺 钛 烤瓷 界面 微观组织 力学性能 

分 类 号：TG425.2[金属学及工艺—焊接]