低温下水热法制备锐钛矿TiO_2晶体材料  

Low-temperature preparation of TiO_2 crystalloid materials via hydrothermal reaction

作　　者：张一兵[1,2] 江雷[2,3] 

机构地区：[1]上饶师范学院,江西上饶334001 [2]国家纳米科学中心,北京100080 [3]中科院化学研究所,北京100080

出　　处：《兵器材料科学与工程》2009年第2期1-4,共4页Ordnance Material Science and Engineering

基　　金：国家"973"计划项目(批准号:2003CB716902);国家"863"计划项目(批准号:2003AA302780)

摘　　要：低温下(90℃)、0.15mol/L的TiCl3的饱和NaCl水溶液加尿素配位剂(尿素/Ti3+摩尔比1/10)用水热法在玻璃基板上制备TiO2晶体材料(粉末和薄膜),SEM和XRD技术表征结果说明,生成的TiO2为锐钛矿型晶体,TiO2粉末是由TiO2纳米棒自组装成的微米球,薄膜则是大面积纳米棒阵列形成。探索低温下制备TiO2纳米材料的最优条件,并讨论反应机理。The TiO2crystalloid materials (powders and thin films) were fabricated on the glass substrates at low-temperature (i.e. 90 ℃) using 0.15 mol/L TiCl3 saturated NaCl aqueous solution adding urea coordinative agent (ratio:urea/ Ti3+1/10)via hy- drothermal reaction. The results of SEM, TEM and XRD techniques show that the TiO2 crystals are anatase, the TiO2 powders are made of microspheres self-assembled by TiO2 nanorods and the TiO2 thin films are arrayed by TiO2 nanorods. The reaction mechanism of forming TiO...

关 键 词：锐钛矿型TiO2 晶体材料 低温 水热法 

分 类 号：TB381[一般工业技术—材料科学与工程]