TiCp/Fe及VCp/Fe复合材料抗氧化性能的研究  

An Investigation on Oxidation Resistance of TiCp/Fe and VCp/Fe Composites

作　　者：李飞龙[1] 苏广才[1] 艾香红[1] 李成[2] 汤宏群[1] 

机构地区：[1]广西大学材料科学与工程学院,广西南宁530004 [2]广西柳州职业技术学院,广西柳州545006

出　　处：《现代铸铁》2009年第2期80-85,共6页Modern Cast Iron

基　　金：广西科学基金资助项目;编号:桂科自0339002;广西教育厅科研项目;编号:200708LX092。

摘　　要：通过向Fe-C母合金中加入钛铁或钒铁合金,形成TiC、VC颗粒增强相,得到抗氧化性能较高的TiCp/Fe、VCp/Fe复合材料;对比试验表明,TiCp/Fe、VCp/Fe复合材料的抗氧化性能明显优于HT250和45钢。由于VCp/Fe复合材料中增强体VC颗粒的体积分数比TiCp/Fe复合材料中的TiC颗粒多、分布更均匀、界面结合更好,因此VCp/Fe比TiCp/Fe复合材料具有更好的抗氧化性能。By adding ferrotitanium and ferrovanadium into Fe-C base alloy to form granule-shaped strengthening phases TiC and VC,the TiCp/Fe and VCp/Fe composites with high oxidation resistance was obtained.Comparison test showed that the oxidation resistance of the TiCp/Fe and VCp-Fe composites was obviously higher than that of the 250 grade gray iron and 45 grade carbon steel.Because VC granules in VCp-Fe composite has higher volume fraction,distribute more uniformly and has better interface junction compared with t...

关 键 词：TICP/FE复合材料 VCP/FE复合材料 抗氧化性能 

分 类 号：TB33[一般工业技术—材料科学与工程]