Synthesis of ITQ-2 zeolite under static conditions and its properties  

作　　者：LIU Baijun HUO Huijuan MENG Qingmin GAO Shansong 

机构地区：[1]Key Laboratory of Catalysis of China National Petroleum Corporation, China University of Petroleum, Beijing 102249, China Key Laboratory of Catalysis of China National Petroleum Corporation, China University of Petroleum, Beijing 102249, China Key Laboratory of Catalysis of China National Petroleum Corporation, China University of Petroleum, Beijing 102249, China Key Laboratory of Catalysis of China National Petroleum Corporation, China University of Petroleum, Beijing 102249, China

出　　处：《Science China Chemistry》2006年第2期148-154,共7页中国科学（化学英文版）

摘　　要：Using silica gel as the precursor, MCM-22(p) was synthesized under the static conditions. Then ITQ-2 zeolite was obtained by using n-cetyltrimethylammonium bromide (CTAB) and tetrapro- pylammonium hydroxide (TPAOH) as the swelling agents to swell the pores of MCM-22(p). The ob- tained zeolite was characterized by XRD, SEM, BET, NH3-TPD. The results show that the zeolite had the best swelling when MCM-22(p):CTAB:TPAOH=1:4:1. The synthesis duration and temperature did not influence significantly the pore swelling. Except TPAOH, CTAB can also be used together with tetrabuthylammonium hydroxide (TBAOH) as the pore swelling agent. There was contribution of sur- face area and pore volume from the mesoporous pores in the ITQ-2 zeolite and it also showed weaker acidity than MCM-22. However, the ITQ-2 supported NiW catalyst showed higher activity and selec- tivity to the middle distillates in the hydrocracking of vacuum gasoil (VGO) than MCM-22 supported catalyst. This implied that the diffusion of large molecules of heavy oil in the catalyst was facilitated due to the presence of the mesoporous pores and hence higher activity and selectivity to middle dis- tillates.Using silica gel as the precursor, MCM-22(p) was synthesized under the staticconditions. Then ITQ-2 zeolite was obtained by using n-cetyltrimethylammonium bromide (CTAB) andtetrapro-pylammonium hydroxide (TPAOH) as the swelling agents to swell the pores of MCM-22(p). Theobtained zeolite was characterized by XRD, SEM, BET, NH_3-TPD. The results show that the zeolite hadthe best swelling when MCM-22(p):CTAB:TPAOH = 1:4:1. The synthesis duration and temperature did notinfluence significantly the pore swelling. Except TPAOH, CTAB can also be used together withtetrabuthylammonium hydroxide (TBAOH) as the pore swelling agent. There was contribution of surfacearea and pore volume from the mesoporous pores in the ITQ-2 zeolite and it also showed weakeracidity than MCM-22. However, the ITQ-2 supported NiW catalyst showed higher activity andselectivity to the middle distillates in the hydrocracking of vacuum gasoil (VGO) than MCM-22supported catalyst. This implied that the diffusion of large molecules of heavy oil in the catalystwas facilitated due to the presence of the mesoporous pores and hence higher activity andselectivity to middle distillates.

关 键 词：STATIC crystallization  ZEOLITE ITQ-2  SWELLING agent  delaminated zeolite  hydrocracking. 

分 类 号：N[自然科学总论]