PREPARATION AND PROPERTIES OF ETHYL-CYANOETHYL CELLULOSE/POLYACRYLIC ACID COMPOSITE FILMS WITH REFLECTION COLORS  

作　　者：Yong Huang Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080 China Laboratory of Cellulose and Lignocellulosics Chemistry Guangzhou Institute of Chemistry Chinese Academy of Sciences, Guangzhou 510650, China 

出　　处：《Chinese Journal of Polymer Science》2001年第3期277-282,共6页高分子科学（英文版）

基　　金：The financial support from the National Natural Science Foundation of China and the National Key Projects of Basic Research-Macromolecular Condensed State is gratefully appreciated.

摘　　要：Ethyl-cyanoethyl cellulose [(E-CE)C]/acrylic acid (AA) becomes a cholesteric liquid crystalline solution withvivid colors when the (E-CE)C concentration is 42 wt%～52 wt%. (E-CE)C/polyacrylic acid (PAA) composites withcholesteric structure were prepared by polymerzing AA in (E-CE)C/AA liquid crystalline solutions. The layers of orderedpolymer chains in the cholesteric phase were inclined during polymerization and the degree of the inclination depended onthe polymerization temperature and the concentration of the solution before polymerization. The cholesteric structure in thecomposites could not be changed when temperature was lower than 100℃. Cross-linking of the PAA in compositesimproved their water-resistance. The cholesteric order of the composites without cross-linking was destroyed when theywhere immersed in water. The color derived from the selective reflection of the cholesteric phase of the cross-linkedcomposites turned from blue to red after the composites absorbed water. The color of the composites could be returned to theoriginal one when the absorbed water was removed from the swollen composites.Ethyl-cyanoethyl cellulose [(E-CE)C]/acrylic acid (AA) becomes a cholesteric liquid crystalline solution withvivid colors when the (E-CE)C concentration is 42 wt%～52 wt%. (E-CE)C/polyacrylic acid (PAA) composites withcholesteric structure were prepared by polymerzing AA in (E-CE)C/AA liquid crystalline solutions. The layers of orderedpolymer chains in the cholesteric phase were inclined during polymerization and the degree of the inclination depended onthe polymerization temperature and the concentration of the solution before polymerization. The cholesteric structure in thecomposites could not be changed when temperature was lower than 100℃. Cross-linking of the PAA in compositesimproved their water-resistance. The cholesteric order of the composites without cross-linking was destroyed when theywhere immersed in water. The color derived from the selective reflection of the cholesteric phase of the cross-linkedcomposites turned from blue to red after the composites absorbed water. The color of the composites could be returned to theoriginal one when the absorbed water was removed from the swollen composites.

关 键 词：Cholesteric structure Composites Selective reflection Liquid crystalline solutions 

分 类 号：TQ317[化学工程—高聚物工业]