SYNTHESIS AND OPTICAL PROPERTIES OF A NOVEL ORGANIC/INORGANIC HYBRID NONLINEAR OPTICAL POLYMER VIA SOL-GEL PROCESS  

作　　者：Hong-xia Xi Zhong Li Zhao-xi Liang The Institute of Chemical Engineering South China University Guangzhou 510640 China The Institute of Polymer Science, Zhongshan University Guangzhou 510275, China 

出　　处：《Chinese Journal of Polymer Science》2001年第4期421-427,共7页高分子科学（英文版）

基　　金：This work was supported by the Postdoctoral Science Foundation of Guangdong Province (No. 9644) and the Natural Science Fund of Guangdong Province(No. 990629).

摘　　要：A new organic/inorganic hybrid nonlinear optical (NLO) material was developed by the sol-gel process of an alkoxysilane dye with tetraethoxysilane. A NLO moiety based on 4-nitro-4 ' -hydroxy azobenzene was covalently bonded to the triethoxysilane derivative, i.e, gamma -isocyanatopropyl triethoxysilane. The preparation process and properties of the sol-gel derived NLO polymer were studied and characterized by SEM, FTIR,H-1-NMR, UV-Vis, DSC and second harmonic generation (SHG) measurement. The results indicated that the chemical bonding of the chromophores to the inorganic SiO2 networks induces low dipole alignment relaxation and preferable orientational stability. The SHG measurements also showed that the bonded polymer film containing 75 wt% of the akoxysilane dye has a high electro-optic coefficient (r(33)) of 7.1 pm/V at 1.1 mum wavelength, and exhibit good SHG stability, the r(33) values can maintain about 92.7% of its initial value at room temperature for 90 days, and can maintain about 59.3% at 100 degreesC for 300 min.A new organic/inorganic hybrid nonlinear optical (NLO) material was developed by the sol-gel process of an alkoxysilane dye with tetraethoxysilane. A NLO moiety based on 4-nitro-4 ' -hydroxy azobenzene was covalently bonded to the triethoxysilane derivative, i.e, gamma -isocyanatopropyl triethoxysilane. The preparation process and properties of the sol-gel derived NLO polymer were studied and characterized by SEM, FTIR,H-1-NMR, UV-Vis, DSC and second harmonic generation (SHG) measurement. The results indicated that the chemical bonding of the chromophores to the inorganic SiO2 networks induces low dipole alignment relaxation and preferable orientational stability. The SHG measurements also showed that the bonded polymer film containing 75 wt% of the akoxysilane dye has a high electro-optic coefficient (r(33)) of 7.1 pm/V at 1.1 mum wavelength, and exhibit good SHG stability, the r(33) values can maintain about 92.7% of its initial value at room temperature for 90 days, and can maintain about 59.3% at 100 degreesC for 300 min.

关 键 词：sol-gel process nonlinear optical material alkoxysilane dye dipole alignment relaxation CHROMOPHORE 

分 类 号：TQ317[化学工程—高聚物工业]