高压低密度聚乙烯绝缘电缆料2210H的性能改进  

Performance improvement of cable insulation grade high pressure low density polyethylene 2210 H

作　　者：熊华伟[1] 杨大伟[1] 赵东波[1] 刘兴旺[1] 

机构地区：[1]中国石油兰州石化公司乙烯厂,甘肃兰州730060

出　　处：《石化技术与应用》2010年第2期128-130,共3页Petrochemical Technology & Application

摘　　要：针对中国石油兰州石化公司高压聚乙烯装置新开发绝缘电缆料2210 H存在介电性能差、交联能力弱的缺陷,采用增大弛放气排放量的同时提高丙烯用量、降低丙醛用量的方法,使系统杂质含量降低,产品介电损耗减小至(1.4~1.9)×10-4,介电常数为2.24;采用逐步提高1~4反应器反应温度的方法,将反应压力从258~262 MPa降低至256~259 MPa,使产品支化度由15.4~15.7上升至15.7~16.3。应用结果表明,改进后2210 H的介电损耗在市场同类产品中最小,其支化度较高,仅需添加2%(质量分数)交联剂过氧化二异丙苯即可达到交联要求。In accordance with the defects of cable insulation grade product 2210 H lately produced in the high pressure low density polyethylene unit of Lanzhou Petrochemical Company,such as poor dielectric property and low cross-linking ability,by increasing purge gas emission and adding propylene instead of a part of propylaldehyde,the impurities content in the reaction system were decreased,the dielectric loss angle tangent of the product decreased to(1.4-1.9)× 10-4,and the dielectric constant were 2.24.By means of...

关 键 词：聚乙烯 高压低密度聚乙烯 绝缘电缆料 介电损耗 交联 支化度 凝胶含量 

分 类 号：TQ325.12[化学工程—合成树脂塑料工业]