高性能钢纤维混凝土的制备与力学性能研究  

Research on preparation and mechanical properties of high performance steel fiber reinforced concrete

作　　者：高乐[1] 

机构地区：[1]广州大学土木工程学院,广东广州510006

出　　处：《山东交通科技》2011年第3期21-23,共3页

基　　金：广东省自然科学基金项目资助;项目编号:06301038;建设部科研开发项目资助;项目编号:06-K1-37;07-K4-5;07-K4-13;10-K3-27;10-K4-18

摘　　要：采用普通硅酸盐水泥、超细粉煤灰、硅灰、高效减水剂、钢纤维和石英砂等原材料,使用常规的制备工艺,配制出钢纤维体积率(Vf)为0～5%的高性能钢纤维混凝土(HPSFRC),并且测试出其抗压强度。采用杆径为40 mm的霍普金森压杆装置对HPSFRC试块进行冲击试验,测出其在冲击荷载作用下的动态抗压强度。最后根据实验数据分析了钢纤维体积率、粉煤灰及硅灰质量分数对HPSFRC静、动态抗压强度的影响。With routine materials such as ordinary portland cement,ultra-fine fly ash,silica fume,superplasticizer,steel fibers and quartz sand,and using conventional mixing and curing conditions to configure High Performance Steel Fiber Reinforced Concrete(HPSFRC) which contain 0～5% steel fiber and test the compressive strength of HPSFRC.Dynamic compressive strength of HPSFRC was tested by the Φ40mm split Hopkinson Press Bar.At last,the influence of steel fiber volume ratio,fly ash and silica fume content on static and dynamic compressive strength of HPSFRC is analyzed based on experimental data.

关 键 词：高性能 钢纤维 SHPB 力学性能 

分 类 号：TU5[建筑科学—建筑技术科学]