Piezoelectric properties of low loss and high Curie temperature (Bi, La)FeO_3-Pb(Ti, Mn)O_3 ceramics with Mn doping  

作　　者：SHI Guiyang, WANG Dalei, BU Shundong, JIN Dengren, and CHENG Jinrong School of Materials Science and Engineering, Shanghai University, Shanghai, 200072, China 

出　　处：《Rare Metals》2012年第6期595-598,共4页稀有金属（英文版）

基　　金：financially supported by National Nature Science Foundation of China(No.50872080);Shanghai Special Foundation of Nanotechnology(No.1052nm07300);Shanghai Education Development Foundation(No.08SG41);Shanghai Leading Academic Disciplines(No.S30107);Innovational Foundation of Shanghai University

摘　　要：Piezoelectric ceramics of 0.6(Bi0.9La0.1)FeO3-0.4Pb(Ti1-xMnx)O3 (BLF-PTM) for x=0, 0.01, 0.02, and 0.03 were prepared by sol-gel process combined with a solid-state reaction method. The tan? for BLF-PTM of x=0.01 is just 0.006 at 1 kHz, drastically decreasing by using Mn dopants. The TC increases to 490 ℃ for BLF-PTM of x=0.02. Furthermore, Mn modification effectively enhances the poling state and the piezoelectric properties of BLF-PTM. The kp, Qm, d33, and g33 of 0.34, 403, and 124 pC1·N-1 and 37×10-3 Vm·N-1 are achieved for BLF-PTM of x=0.01. The results indicate that Mn modified BLF-PTM is a competitive high power and high temperature piezoelectric material with excellent piezoelectric properties.Piezoelectric ceramics of 0.6(Bi0.9La0.1)FeO3-0.4Pb(Ti1-xMnx)O3 (BLF-PTM) for x=0, 0.01, 0.02, and 0.03 were prepared by sol-gel process combined with a solid-state reaction method. The tan? for BLF-PTM of x=0.01 is just 0.006 at 1 kHz, drastically decreasing by using Mn dopants. The TC increases to 490 ℃ for BLF-PTM of x=0.02. Furthermore, Mn modification effectively enhances the poling state and the piezoelectric properties of BLF-PTM. The kp, Qm, d33, and g33 of 0.34, 403, and 124 pC1·N-1 and 37×10-3 Vm·N-1 are achieved for BLF-PTM of x=0.01. The results indicate that Mn modified BLF-PTM is a competitive high power and high temperature piezoelectric material with excellent piezoelectric properties.

关 键 词：piezoelectric property low loss high Curie temperature poling state 

分 类 号：TQ174.1[化学工程—陶瓷工业]