流变法研究铜对Lyocell纤维纺丝原液热稳定性的影响  

Influece of Copper on the Thermal Stability of the Lyocell Fiber Spinning Solution

作　　者：许虎[1,2] 徐鸣风[1] 程春祖[1] 徐纪刚[1] 孙玉山[1] 骆强[1] 赵庆章[1] 

机构地区：[1]中国纺织科学研究院生物源纤维制造技术国家重点实验室,北京100025 [2]天津工业大学材料科学与工程学院,天津300387

出　　处：《合成纤维》2012年第12期13-16,共4页Synthetic Fiber in China

基　　金：国家973项目(2012CB724610;2010CB735805);"十二五"科技支撑计划项目(2011BAE11B02)

摘　　要：在N-甲基吗啉-N-氧化物(NMMO)溶解纤维素制得Lyocell纤维的过程中,在纺丝液中添加金属铜粉,采用流变仪快速测定低剪切速率下纺丝原液的流变性,研究了纺丝原液热稳定性的问题。结果表明:随着温度的升高,纤维素降解加快;加入铜粉使得纤维素降解加剧;采用流变仪,可快速、简便、有效地测得纺丝原液的热稳定性。Copper powder is added into the spinning solution of cellulose and N-methylmorpholine-N-oxide during the spinning of Lyocell fiber.The rheometer is used to determine fast rheology at the low shear rate.The thermal stability of Lyocell fiber spinning solution is studied.The experiments show that cellulose degradated faster with the temperature increasing and the addition of copper.Thermal stability of spinning solution is measured fast,simplely and effectively by the rheometer.

关 键 词：流变性能 纤维素纺丝液 NMMO 铜 热稳定性 

分 类 号：TQ340.64[化学工程—化纤工业]