两种不同层错能TWIP钢的变形行为及组织演变  

Deformation behavior and microstructure evolution of TWIP steels with different SFE

作　　者：李华英[1] 丁桦[1,2] 李昊泽[1] 邱春林[2] 

机构地区：[1]东北大学材料与冶金学院,沈阳110819 [2]东北大学轧制技术及连轧自动化国家重点实验室,沈阳110819

出　　处：《材料与冶金学报》2012年第3期183-187,共5页Journal of Materials and Metallurgy

基　　金：中央高校基本科研业务费(N100602004);轧制技术及连轧自动化国家重点实验室开放课题(2009001)

摘　　要：对两种不同层错能TWIP钢分别在1 100℃进行了固溶处理,观察了实验钢的微观组织,并分析了实验钢的变形行为.结果表明:通过透射电镜观察,发现较低层错能的TW1实验钢内出现层错,而较高层错能的TW2实验钢内层错较少,但发现位错呈有规则排列的组态;TW2实验钢的加工硬化曲线呈现单调下降的趋势,而TW1实验钢的曲线则分为3个阶段.Two kinds of TWIP steels with different SFE(Stacking Fault Energy) were heat treated at 1 100 ℃ for 1 hour to investigate the microstructure and deformation characteristics.The results show that some stacking faults are only observed in the microstructure of the TW1 steel with a lower SFE value,and rarely found in the TW2 steel with a higher SFE value,but the arrangement of dislocation is regular in the TW2 steel.By the study on the mechanical properties of the steels,the strain hardening rate of TW2 steel decreases with increasing true strain in the whole deformation stage;while the plastic deformation of TW1 steel could be divided into three stages.

关 键 词：层错能 孪晶诱发塑性(TWIP) 固溶处理 形变孪晶 应变硬化率 

分 类 号：TG142.1[一般工业技术—材料科学与工程]