固溶温度对中锰TRIP钢组织与力学性能的影响  

Influence of the solid solution temperature on microstructure and mechanical properties of Mn TRIP steel

作　　者：蒋君[1] 辛啟斌[1] 薛鑫[1] 丁桦[1] 马勇[1] 王莉雅[1] 方烽[1] 

机构地区：[1]东北大学材料与冶金学院,沈阳110004

出　　处：《材料与冶金学报》2012年第3期188-191,196,共5页Journal of Materials and Metallurgy

基　　金：国家大学生创新性实验计划(110132)

摘　　要：以w(Mn)=8%的热轧TRIP钢(即相变诱导塑性钢)为对象,研究了热处理工艺对其显微组织与力学性能的影响规律.该中锰TRIP钢在固溶温度为800℃时,可获得包括铁素体、马氏体、残余奥氏体的多相组织.与一般TRIP钢相比,其力学性能明显提高,在固溶加回火的条件下,实验钢的抗拉强度为800～1 000 MPa,延伸率达到31%～40%,而强塑积达(30～32)GPa%.Based on the hot rolled TRIP steel(transformation induced plasticity steel)with 8% Mn,the influence of the heating processing on the microstructure and mechanical properties of the steel was studied.When the solid solution temperature is 800 ℃,it can get polyphase structure including ferrite、martensite and remaining austenite.Comparied with the common steel,mechanical property of the TRIP steel has a notable improvement.Under the condition of the solid solution and tempering temperature,the tensile strength of the experimental steels is 800~1 000 MPa,the specific elongation is up to 31%~40%,and the product of tensile strength and elongation(TS×T.EL) is up to(30~32)GPa%.

关 键 词：热轧TRIP钢 锰含量 固溶温度 残余奥氏体 力学性能 

分 类 号：TG156.94[金属学及工艺—热处理]