氧化锆喷雾造粒粉末的制备  

Preparation of Zirconia Spherical Particles Based on Spray Method

作　　者：刘春红[1] 李学伟[1] 郑书航[1] 闫磊鑫[1] 张立明[1] 

机构地区：[1]中钢集团洛阳耐火材料研究院有限公司先进耐火材料国家重点实验室,河南洛阳471039

出　　处：《中国粉体技术》2013年第3期55-57,共3页China Powder Science and Technology

摘　　要：为了制备流动性、均匀性好的氧化锆粉末,以氧化钙部分稳定氧化锆为主要原料,采用离心式喷雾造粒干燥机,制备出松装密度为1.945 g/cm3,流动性好且呈球状的氧化锆颗粒.结果表明,均匀稳定性好的氧化锆料浆对制备优良性能的氧化锆颗粒至关重要；喷雾造粒的工艺条件对造粒粉末性能也有较大影响:当雾化器频率为100～110 Hz,进料泵转速为15～20 r/min时,造粒粉末流动性好,颗粒相对均匀,缺陷较少.To prepare uniform zirconia spherical particles with excellent flowability by spray drying process,CaO partly stabilized ZrO2 was used as the main raw materials.The spherical particles with loose density of 1.945 g/cm3with excellent flowability were obtained.The results show that suspensions and spray-dried operating conditions have great influence on the properties of zirconia particles.When the atomizer frequency varies from 100 to 110 Hz and the rotate speed of pump varies from 15 to 20 r/min,the uniform particles have excellent flowability and little defects.

关 键 词：喷雾造粒 工艺条件 松装密度 