Ultraviolet-shielding and conductive double functional films coated on glass substrates by sol-gel process  

作　　者：董玉红 赵青南 吴硕 卢秀强 

机构地区：[1]Jiang Su Xiuqiang Glasswork CO.,Ltd.Suyu District,Suqian City,Jiangsu Province,223800,China [2]Key Laboratory for Silicate Materials Science and Engineering of Ministry of Education,Wuhan University of Technology

出　　处：《Journal of Rare Earths》2010年第S1期446-450,共5页稀土学报（英文版）

基　　金：Project supported by the Special Fund of Jiangsu Province for the Transformation of Scientific and Technological achievements

摘　　要：Ultraviolet-shielding and conductive double functional films were composed of CeO2-TiO2 film and SnO2:Sb film deposited on glass substrates using sol-gel process.Ce(NO3)3·6H2O and Ti(C4H9O4),SnCl4 and SbCl3 were used as precursors of the two different functional films respectively.The CeO2-TiO2 films were deposited on glass substrates by sol-gel dip coating method,and then the SnO2:Sb films with different thickness were deposited on the pre-coated CeO2-TiO2 thin film glass substrates,finally,the substrates coated with double functional films were annealed at different temperatures.The optical and electrical properties of the CeO2-TiO2 films and the double films were measured by UV-Vis spectrometer and four probe resistance measuring instrument.The crystal structures and surface morphology of the films were characterized using XRD and optical microscope,respectively.The obtained results show that the ultraviolet-shielding rate of the glass substrates with CeO2-TiO2 films is not less than 90%,and transmittance in visible lights can reach 65%.With the thickness of the SnO2:Sb film increasing,its conductivity became better,and the surface resistance is about 260 Ω/ when the SnO2:Sb films were deposited 11 cycles of the dip on the pre-coated CeO2-TiO2 glass.The ultraviolet-shielding rate of the glass substrates with double functional films is higher than 97%,and the peak transmittance in the visible lights is 72%.Additionally,with increasing the heat treatment time,the Na+ of the glass substrates diffuses into the films,resulting in the particle size of SnO2 crystal smaller.Ultraviolet-shielding and conductive double functional films were composed of CeO2-TiO2 film and SnO2:Sb film deposited on glass substrates using sol-gel process.Ce(NO3)3·6H2O and Ti(C4H9O4),SnCl4 and SbCl3 were used as precursors of the two different functional films respectively.The CeO2-TiO2 films were deposited on glass substrates by sol-gel dip coating method,and then the SnO2:Sb films with different thickness were deposited on the pre-coated CeO2-TiO2 thin film glass substrates,finally,the substrates coated with double functional films were annealed at different temperatures.The optical and electrical properties of the CeO2-TiO2 films and the double films were measured by UV-Vis spectrometer and four probe resistance measuring instrument.The crystal structures and surface morphology of the films were characterized using XRD and optical microscope,respectively.The obtained results show that the ultraviolet-shielding rate of the glass substrates with CeO2-TiO2 films is not less than 90%,and transmittance in visible lights can reach 65%.With the thickness of the SnO2:Sb film increasing,its conductivity became better,and the surface resistance is about 260 Ω/ when the SnO2:Sb films were deposited 11 cycles of the dip on the pre-coated CeO2-TiO2 glass.The ultraviolet-shielding rate of the glass substrates with double functional films is higher than 97%,and the peak transmittance in the visible lights is 72%.Additionally,with increasing the heat treatment time,the Na+ of the glass substrates diffuses into the films,resulting in the particle size of SnO2 crystal smaller.

关 键 词：ultraviolet-shielding/conductive double functional films CeO2-TiO2 SnO2:Sb Glass substrates sol-gel rare earths 

分 类 号：TB43[一般工业技术]