Effect of heat treatment on mechanical properties of heavily cold-rolled Fe-6.5wt%Si alloy sheet  

作　　者：LIANG YongFeng,YE Feng,LIN JunPin,WANG YanLi,ZHANG LaiQi & CHEN GuoLiang State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing,Beijing 100083,China 

出　　处：《Science China(Technological Sciences)》2010年第4期1008-1011,共4页中国科学（技术科学英文版）

基　　金：supported by the National Basic Research Program of China ("973" Project)(Grant No 2006CB605205-2);the National Natural Science Foundation of China (Grant No 50771018)

摘　　要：Fe-6.5wt%Si alloy has excellent soft magnetic properties,but it is hard to be cold-rolled due to appearance of ordered phases in this alloy.In this paper we report that ultra thin Fe-6.5wt%Si sheet of 0.05 mm thick was obtained by heavily cold rolling.By means of optical microscope,micro-hardness indenter,instron,SEM and X-ray diffraction,the effect of heat treatment on mechanical properties of this alloy sheet was investigated.The heavily cold-rolled sheet exhibits some extent of ductility.The ultimate tensile strength reaches 1.93 GPa.After heat treatment,micro-hardness is decreased and the ductility is lost,especially at temperature above 650℃ when recrystallization takes place.The reason for decreasing the ductility lies in the ordered DO3 phase transformation.Fe-6.5wt%Si alloy has excellent soft magnetic properties,but it is hard to be cold-rolled due to appearance of ordered phases in this alloy.In this paper we report that ultra thin Fe-6.5wt%Si sheet of 0.05 mm thick was obtained by heavily cold rolling.By means of optical microscope,micro-hardness indenter,instron,SEM and X-ray diffraction,the effect of heat treatment on mechanical properties of this alloy sheet was investigated.The heavily cold-rolled sheet exhibits some extent of ductility.The ultimate tensile strength reaches 1.93 GPa.After heat treatment,micro-hardness is decreased and the ductility is lost,especially at temperature above 650℃ when recrystallization takes place.The reason for decreasing the ductility lies in the ordered DO3 phase transformation.

关 键 词：Fe-6.5wt%Si ALLOY COLD ROLLING HEAT treatment microstructure MECHANICAL properties 

分 类 号：TG335.12[金属学及工艺—金属压力加工]