Equilibrium position of misfit dislocation dipole and critical parameters of buried strained nanoscale inhomogeneity in system of viscoelastic matrix  

作　　者：刘又文 谢超 方棋洪 

机构地区：[1]College of Mechanics and Aerospace,Hunan University

出　　处：《Journal of Central South University》2008年第S1期550-554,共5页中南大学学报（英文版）

基　　金：Project(10472030) supported by the National Natural Science Foundation of China

摘　　要：A theoretical model was suggested which describes the generation of the misfit dislocation dipole in the system of the viscoelastic matrix containing a circular stiff nanoscale inhomogeneity.The critical condition of misfit dislocation dipole and the solution of equilibrium position were given.The influence of the ratio of shear modulus,the misfit strain and viscosity on the equilibrium of the dislocation and critical parameter of inhomogeneity was investigated.The result shows that the equilibrium position de increases with the increase of the ratio of original shear modulus and the effect decreases with the increase of viscosity of matrix.Along with the increase of viscosity of matrix,de first increases and then decreases and possesses maximum value when t=0.3τ and tends to a stable value when t≥1.0τ.Along with the increase of viscosity of matrix,Rc first decreases and then increases and possesses minimum value when t=0.3τ and tends to a stable value when t≥1.0τ.A theoretical model was suggested which describes the generation of the misfit dislocation dipole in the system of the viscoelastic matrix containing a circular stiff nanoscale inhomogeneity. The critical condition of misfit dislocation dipole and the solution of equilibrium position were given. The influence of the ratio of shear modulus, the misfit strain and viscosity on the equilibrium of the dislocation and critical parameter of inhomogeneity was investigated. The result shows that the equilibrium position d e increases with the increase of the ratio of original shear modulus and the effect decreases with the increase of viscosity of matrix. Along with the increase of viscosity of matrix, d e first increases and then decreases and possesses maximum value when t=0.3τ and tends to a stable value when t?1.0z. Along with the increase of viscosity of matrix, R c first decreases and then increases and possesses minimum value when t=0.3τ and tends to a stable value when t?1.0τ.

关 键 词：nanoscale INHOMOGENEITY VISCOELASTIC MISFIT strain MISFIT dislocation DIPOLE CRITICAL condition 

分 类 号：O345[理学—固体力学]