工业废渣对水泥生料易烧性影响的试验研究  

作　　者：兰明章[1] 崔素萍[1] 严兴李[1] 

机构地区：[1]北京工业大学材料学院,北京100024

出　　处：《水泥》2004年第6期7-9,共3页Cement

基　　金：国家重点基础研究发展规划(973)项目(2001CB610700)

摘　　要：应用XRD和化学分析等方法对利用铜渣、磷渣、铅锌渣等工业废渣来改善高C3S配料的水泥生料易烧性进行试验研究。研究表明:铜渣、铅锌渣对改善高C3S配料的水泥生料易烧性效果不明显,掺入适量磷渣可很好地改善水泥生料的易烧性。The method of XRD and chemical analysis was applied to study how to improve the burnability of cement raw meal with high content of C3S batching by using the waste industrial slag such as copper slag, phosphor slag and lead-zinc slag. The result shows that the burnability of cement raw meal with high content of C3S batching was improved with suitable content of phosphor slag, but the effect of copper slag and lead-zinc slag was not that obvious.

关 键 词：工业废渣 水泥 生料 易烧性 试验 微量组分 

分 类 号：TQ172.44[化学工程—水泥工业]