穿甲弹侵彻装甲板时绝热剪切带的产生及对侵彻过程影响  

The Shape and Effect of the Adiabatic Shear Band on the Armor Plate impacted by the Penetration

作　　者：荣光[1] 黄德武[2] 易文俊[1] 王中原[1] 汤瑞峰[1] 

机构地区：[1]南京理工大学,江苏南京210094 [2]沈阳工业学院,辽宁沈阳110015

出　　处：《弹箭与制导学报》2003年第S3期289-291,共3页Journal of Projectiles,Rockets,Missiles and Guidance

基　　金：南京理工大学弹道国防重点实验室资助(98JS33.5.1QT2801)

摘　　要：用钨合金小口径穿甲弹对30CrMnMo 装甲钢板做射击侵彻试验,并利用扫描电镜和光学金相显微镜研究了其显微组织结构变化。发现了从弹孔表面到靶板内部的微观结构是分层逐渐变化的,还发现在弹孔周围出现了三类绝热剪切带,并结合试验中的宏观现象,对绝热剪切带的成因,形貌及对装甲板破坏过程的影响进行了分析。The experiments of the penetration made of W alloys impacted on the 30CrMnMo armor target steel plate were performed.Microstructures of the penetrated hole in the 30CrMnMo steel plate are studied using SEM and optical metallography.It was found that from the penetrated surface of the hole to the interior of the steel plate,the microstructures of materials is changeable the layer to layer.The three types of adiabatic shear bands were found and the initial causes and the effect to damages of armor target were also analysed.

关 键 词：显微组织 绝热剪切带 高速侵彻 

分 类 号：TJ410.6[兵器科学与技术—火炮、自动武器与弹药工程]