RAMAN AND IR SPECTROSCOPY OF PTCR Ba_(1-x)Pb_xTiO_3 CERAMICS  

作　　者：王国梅 雷家珩 恽怀顺 薛理辉 王勤 

出　　处：《Journal of Wuhan University of Technology(Materials Science)》1995年第4期57-64,共8页武汉理工大学学报（材料科学英文版）

摘　　要：Raman and IR spectra of Nb-doped PTC Ba1-xPbxTiO3 semiconducting ceramics (x = 0,0. 28,0. 296,0. 313,0. 330,0. 370) have been measured, and mode assignments of Raman scattering frequencies and infrared absorption peaks have been made at room temperature. The influence of Pb2+ ions content on resistivity temperature characteristics and vibration spectra for the Ea1-xPbxTiO3, ceramics have been discussed,and the temperature dependence of the Raman spectra in tetragonal and cubic phases have been investigated from 25 to 340℃. The results indicated that the Raman spectra of the paraelectric phase above Curie point are obviously different from that of ferroelectric phase below Curie point are obviously different from that of ferroelectric phase below Curie point for all the samples. Curie point of each sample,which is determined by resistivity-temperature characteristic measurment, is in good agreement with the results of Raman analysis. The ferroelectric phase transition in the PTCR Bai-xPbxTiO3 ceramics belongs to a distortion or displacement transition.Raman and IR spectra of Nb-doped PTC Ba1-xPbxTiO3 semiconducting ceramics (x = 0,0. 28,0. 296,0. 313,0. 330,0. 370) have been measured, and mode assignments of Raman scattering frequencies and infrared absorption peaks have been made at room temperature. The influence of Pb2+ ions content on resistivity temperature characteristics and vibration spectra for the Ea1-xPbxTiO3, ceramics have been discussed,and the temperature dependence of the Raman spectra in tetragonal and cubic phases have been investigated from 25 to 340℃. The results indicated that the Raman spectra of the paraelectric phase above Curie point are obviously different from that of ferroelectric phase below Curie point are obviously different from that of ferroelectric phase below Curie point for all the samples. Curie point of each sample,which is determined by resistivity-temperature characteristic measurment, is in good agreement with the results of Raman analysis. The ferroelectric phase transition in the PTCR Bai-xPbxTiO3 ceramics belongs to a distortion or displacement transition.

关 键 词：raman  IR  spectroscopy PTCR Ba1-x PbxTiO3 ceramics 

分 类 号：TQ174[化学工程—陶瓷工业]