汽轮机叶片钢X22CrMoV12-1的研制  

Development of turbine blade steel X22CrMoV12-1

作　　者：张丽娜[1] 李骥[1] 陈德利[1] 郭仁辉[1] 

机构地区：[1]抚顺特殊钢股份有限公司技术中心,辽宁抚顺113001

出　　处：《金属热处理》2015年第6期167-170,共4页Heat Treatment of Metals

摘　　要：对X22CrMoV12-1钢的化学成分进行了优化设计,并对X22CrMoV12-1钢热处理工艺进行了研究。结果表明,相同回火温度下,微调淬火温度对室温力学性能影响不大;相同淬火温度下,随回火温度提高,材料韧性提高,强度降低。采用1020℃淬火+690℃回火的热处理工艺,可获得优良的综合力学性能,可用于实际生产。Chemical composition of X22CrMoV12-1 steel was optimized and heat treatment processes of the steel were studied. The results show that at the same tempering temperature,the small change of the quenching temperature has little effect on the mechanical properties at room temperature,while as tempering temperature increase,the toughness of the steel is improved,and the strength decrease at the same quenching temperature. The steel can get excellent comprehensive mechanical properties when quenched at 1020 ℃ and then tempered at 690 ℃,which can be used to production.

关 键 词：X22CrMoV12-1钢 热处理 力学性能 

分 类 号：TG142.45[一般工业技术—材料科学与工程] TG161[金属学及工艺—金属材料]