等离子体法制备超细粉体氮化铝的研究  

Research on preparation of ultra-fine powder of aluminum nitride by plasma

作　　者：尚书勇[1] 梅丽[1] 李兰英[1] 印永祥[1] 戴晓雁[1] 

机构地区：[1]四川大学化工学院,成都610065

出　　处：《化工新型材料》2004年第7期8-10,共3页New Chemical Materials

基　　金：国家科技部中小型企业科技创新基金项目 (0 1C2 62 2 51 0 0 958)

摘　　要：以微米级铝粉为原料 ,用N2 热等离子体法制备了超细氮化铝粉体。在等离子体功率12kW ,运行N2 流量 2m3/h ,急冷NH3流量 0 6m3/h ,送粉N2 流量 0 8m3/h条件下 ,铝粉全部转化为纳米氮化铝。采用SEM技术和粒度分析仪对产品进行了分析 ,制得的氮化铝粉末平均粒径为10 0nm ,粒度分布为 4 0～ 14Ultra-fine powder of aluminum nitride were produced by evaporation of micron aluminum powder at nitrogen thermal plasma.The experimental result shows,the aluminum powder completely translated into aluminum nitride at the conditions as follows.Power:12kW;Operation gas:N 2,2m 3/h;Refrigerant gas:NH 3,0.6m 3/h;Carried gas:N 2,0.8m 3/h.Size range of aluminum nitride particle was measured to be from 40nm to 140nm,average size is 100nm .It was measured by scanning electric mirror(SEM) and particle size analyzer.

关 键 词：氮气等离子体法 制备 超细粉体材料 氮化铝 微米级铝粉 N2 SEM技术 粒度分析仪 合成纳米材料 

分 类 号：TB383[一般工业技术—材料科学与工程]