高沸醇木质素改性丁腈橡胶  

Modification of NBR with HBS Lignin

作　　者：许金仙[1] 程贤甦[1] 陈云平[1] 林春莺[1] 

机构地区：[1]福州大学材料科学与工程学院,福建福州350002

出　　处：《特种橡胶制品》2004年第5期1-4,共4页Special Purpose Rubber Products

基　　金：福建省教育厅科研基金B类项目(JB02058);福州市科技计划资助项目(2002 06)。

摘　　要：高沸醇(HBS)木质素是用高沸醇溶剂法从松木、稻草中提取的一种新型的环保材料。研究了HBS木质素羟甲基化改性后共沉物对NBR补强效果的影响。由产物的红外光谱可知,HBS木质素的羟甲基化是可以进行的。试验结果表明,添加HBS木质素能改善NBR的性能,尤其是拉断伸长率有明显的提高,还有良好的耐老化性能,明显优于炭黑。HBS(High Boiling Solvent)lignin was extracted from pine of rice straws by using high boiling alcohol as a solvent.HBS lignin is a novel environment friendly material.According to IR spectra analysis,it was found that HBS lignin could be modified by hydroxymethylation with formaldehyde.The properties of NBR-modified lignin composites were investigated.Mechanical test results showed that modified HBS lignin could improve the properties of NBR,especially the elongation at break.The anti-aging properties of HBS lignin modefied NBR was better than that of carbon black modified NBR.

关 键 词：高沸醇木质素 丁腈橡胶 红外光谱 