Dependence of Magnetic Properties of Rapidly Quenching (Nd,Pr)_x (FeCoZr)_(94-x)B_6 Bonded Magnets on Rare Earths Content  

作　　者：查五生 刘颖 高升吉 连利仙 涂铭旌 

机构地区：[1]College of Material Science & Engineering, Sichuan University, Chengdu 610065, China [2]College of Material Science & Engineering, Xihua University, Chengdu 610039, China

出　　处：《Journal of Rare Earths》2004年第3期418-421,共4页稀土学报（英文版）

基　　金：Projectsupportedby 863Project ( 2 0 0 1AA3 2 40 3 0 )

摘　　要：By using sub-overquenching and annealing method which has a wide processing window, (Nd, Pr), ( Fe-CoZr)(94-x)B-6(x = 12, 10.5, 10, 9) bonded magnets were prepared and the effect of rare earths content on magnetic properties was investigated. Being spun at sub-ove.quenching speed the as-spun ribbons consist of amorphous phases mixed with fine crystallites. After crystallization under optimum annealing conditions and bonded with 3.25% (mass fraction) epoxy, the magnets obtained the optimum magnetic properties. The rare earths content directly determines the magnetic properties. With the reduction of rare earths content, B-r increases but H-ci and (BH)(max) decrease. x = 10 is the critical value for the magnetic proper-ties change. Below this value, Br increases slowly meanwhile H-ci and (BH)(max) decrease strongly because alloy contains extra fractions of soft magnetic phase which are not coupled with the hard magnetic phase.. This experimental result is consistent with the calculated results using the model of volume fraction of soft magnetic phase coupled completely suggested.By using sub-overquenching and annealing method which has a wide processing window, (Nd, Pr), ( Fe-CoZr)(94-x)B-6(x = 12, 10.5, 10, 9) bonded magnets were prepared and the effect of rare earths content on magnetic properties was investigated. Being spun at sub-ove.quenching speed the as-spun ribbons consist of amorphous phases mixed with fine crystallites. After crystallization under optimum annealing conditions and bonded with 3.25% (mass fraction) epoxy, the magnets obtained the optimum magnetic properties. The rare earths content directly determines the magnetic properties. With the reduction of rare earths content, B-r increases but H-ci and (BH)(max) decrease. x = 10 is the critical value for the magnetic proper-ties change. Below this value, Br increases slowly meanwhile H-ci and (BH)(max) decrease strongly because alloy contains extra fractions of soft magnetic phase which are not coupled with the hard magnetic phase.. This experimental result is consistent with the calculated results using the model of volume fraction of soft magnetic phase coupled completely suggested.

关 键 词：metal materials Pr-based permanent magnets nanocrystalline composite magnetic properties completely coupling model rare earths 

分 类 号：TM273[一般工业技术—材料科学与工程]