A Study on Alnico Permanent Magnet Powders Prepared by Atomization  

作　　者：ChangbinSONG BocksooHAN YingLI 

机构地区：[1]DivisionofMaterialsEngineering,KongjuNationalUniversity,Kongju,Korea [2]DivisionofmechanicalEngineering,HanbatNationalUniversity,Taejon,Korea [3]InstituteofMaterials,ShanghaiUniversity,Shanghai200072,China

出　　处：《Journal of Materials Science & Technology》2004年第3期347-349,共3页材料科学技术（英文版）

摘　　要：Alnico powders were prepared by gas atomization process. Composition of the Alnico powders was Fe37.1 A18.2Ni17.6-Co26.6 Cu3.3 Ti7.2 (wt pct) which was the same as that of commercially available Alnico magnets. Averageparticle size of the powders was 119μm. Effects of heat treatment in magnetic field on magnetic properties of thepowders were investigated. The optimum process of heat treatment was found as follows, heated at 870℃ for 1min first, then cooled down to 700℃ at cooling rate 0.3℃/s in magnetic field, and finally aged isothermally for 4 h.Magnetic properties of the Alnico powders were measued and the results were that intrinsic coercivity i_H_c was 1.0kOe and remanence M_r was 36.5 emu/g.Alnico powders were prepared by gas atomization process. Composition of the Alnico powders was Fe37.1 A18.2Ni17.6-Co26.6 Cu3.3 Ti7.2 (wt pct) which was the same as that of commercially available Alnico magnets. Averageparticle size of the powders was 119μm. Effects of heat treatment in magnetic field on magnetic properties of thepowders were investigated. The optimum process of heat treatment was found as follows, heated at 870℃ for 1min first, then cooled down to 700℃ at cooling rate 0.3℃/s in magnetic field, and finally aged isothermally for 4 h.Magnetic properties of the Alnico powders were measued and the results were that intrinsic coercivity i_H_c was 1.0kOe and remanence M_r was 36.5 emu/g.

关 键 词：Gas atomization Alnico magnetic powder 

分 类 号：TM273[一般工业技术—材料科学与工程]