SiC_p/Al复合材料制备工艺对组织与性能的影响  

The effect of fabricating processes on the microstructure and properties of SiC_p/Al composites

作　　者：张维玉[1] 左涛[1] 肖伯律[1] 樊建中[1] 田晓风[1] 

机构地区：[1]北京有色金属研究总院国家有色金属复合材料工程技术研究中心,北京100088

出　　处：《粉末冶金技术》2004年第6期354-358,共5页Powder Metallurgy Technology

摘　　要：采用高能球磨粉末冶金法制备了体积分数为 15 %SiCp/ 2 0 0 9Al复合材料 ,研究了球磨转速、球磨时间对复合材料组织和性能的影响。结果表明 ,球磨转速和球磨时间是影响复合材料力学性能的重要因素 ,较长时间高转速球磨使得SiC颗粒均匀分布 ,转速 190r/min、球磨 6h制备的复合粉末经真空热压、挤压后的复合材料SiC颗粒均匀分布 ,材料的抗拉强度高达 6 5 0MPa,伸长率大于 5 %。A 15vol%SiC p/2009Al composites was fabricated through high energy milling with powder metallurgy (PM) technique. Effect of rotational speed and time of milling on mechanical properties of composites was investigated. The results indicate that the two factors above are important to properties of composites. Long time and high speed of milling make a uniform distribution of SiC particle. The composite hot-pressed and extruded with powder milled at speed of 190r/min for 6 hours has uniform SiC distribution, tensile strength of 650 MPa and elongation of 5%.

关 键 词：组织与性能 组织和性能 SICP/AL复合材料 球磨时间 SIC颗粒 挤压 伸长率 真空热压 复合材料力学 粉末冶金法 

分 类 号：TF123[冶金工程—粉末冶金] TB333[冶金工程—冶金物理化学]