GMA熔融接枝SBS及其对PA6增容研究  被引量:6

GLYCIDYL METHACRYLATE MELT GRAFTING SBS AND ITS TOUGHENING EFFECT ON PA6

在线阅读下载全文

作  者:李海东[1] 王宇明[1] 白福臣[2] 刘秀奇[1] 

机构地区:[1]长春工业大学化学工程学院,长春130012 [2]中国科学院长春应用化学研究所,长春130022

出  处:《工程塑料应用》2005年第2期8-11,共4页Engineering Plastics Application

基  金:973资助项目(G1999064800)

摘  要:   采用活性单体甲基丙烯酸缩水甘油酯(GMA)对(苯乙烯 /丁二烯 /苯乙烯)嵌段共聚物 (SBS)进行熔融接枝,制备了GMA接枝SBS(SBS- g -GMA)。用化学滴定方法测定其接枝率,考察了单体GMA和引发剂过氧化二异丙苯的用量对接枝率的影响;测试了尼龙 6(PA6) /SBS- g -GMA共混物的拉伸性能和冲击性能,并用扫描电子显微镜观察了PA6 /SBS- g -GMA共混物的形态结构。结果表明,用SBS -g -GMA增韧PA6可获得很好的效果。SBS was grafted with reactive monomor GMA by melt grafting, and SBS-g-GMA was obtained. The graft ratio of SBS-g-GMA was measured with chemical titrimetry, and the effects of monomor GMA and initiator DCP contents on graft ratio were examined. The tensile properties and impact properties of PA6/SBS-g-GMA were tested and its morphology was observed with SEM. The results showed that SBS-g-GMA had a good toughening effect on PA6.

关 键 词:SBS 熔融接枝 GMA 接枝率 共混物 PA 活性单体 观察 效果 影响 

分 类 号:TQ325[化学工程—合成树脂塑料工业] TQ334

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象