Cu-P系稀土耐候钢中最佳稀土含量的研究  

Optimal Rare Earths Content in Cu-P-RE Weathering Steels

作　　者：岳丽杰[1] 王龙妹[2] 徐成海[1] 朴秀玉[3] 

机构地区：[1]东北大学机械工程与自动化学院,辽宁沈阳110004 [2]北京钢铁研究总院冶金工艺所,北京100081 [3]北京科技大学冶金与生态工程学院,北京100083

出　　处：《中国稀土学报》2004年第6期816-820,共5页Journal of the Chinese Society of Rare Earths

基　　金：国家"十五"科技攻关项目(2002BA315A-5)

摘　　要：利用光学显微镜、图像分析仪和电子探针对低氧低硫的10PCuRE耐候钢板坯进行了观察和检测,采用干 湿周浸室内加速试验方法测得了试验钢的腐蚀率。用电化学方法测得了带锈样的阳极极化曲线。研究得出对于S:～0.004%,O:～0.002%的10PCuRE耐候钢,最佳稀土含量为0.0065%～0.012%,此稀土含量对非金属夹杂物的变质作用和耐蚀性能的提高最为有利。10PCuRE steel slabs whose contained low of oxygen and sulfur were analyzed with metallograph, image analyzer and EPMA. Corrosion rates of RE weathering steel were obtained by dry-wet immersion test. The anode polarization curves of testing steel were measured by electrochemical methods. It is concluded that the optimal RE content is 00065%～0012% to 10PCuRE steel contained oxygen and sulfur about 0002% and 0004% respectively. The RE content is the most favorable to controlling inclusion types and morphologies and improving corrosion resistance of weathering steel.

关 键 词：金属材料10PCuRE钢 夹杂物 耐蚀性 稀土 

分 类 号：TG113.23[金属学及工艺—物理冶金]