作　　者：李英[1] 马秀良[1] 

机构地区：[1]中国科学院金属研究所沈阳材料科学国家(联合)实验室,辽宁沈阳110016

出　　处：《电子显微学报》2004年第6期609-612,共4页Journal of Chinese Electron Microscopy Society

基　　金：国家杰出青年基金项目(No.50325101);国家重点基础研究发展规划(973)项目(2002CB613503)资助.

摘　　要：利用X射线衍射仪(XRD)、X射线能谱仪(EDS)、扫描电子显微镜(SEM)以及透射电子显微镜(TEM)等实验手段对热蒸发ZnO粉末产物的形貌、组成成分、两种相的取向关系以及微观结构进行了表征。结果表明:实验所得到的制备产物由Zn ZnO纳米电缆组成,电缆的直径在50～200nm之间而长度可达几百微米。电缆由单质Zn组成的芯和由ZnO组成的外壳组成。两相具有两种比较固定的取向关系[1120]Zn [1120]ZnO和[0001]Zn [0001]ZnO。Zn/ZnO nanocables have been synthesized successfully via simply evaporating ZnO powders at high temperature. X-ray diffraction clarified that the as-received product is composed of Zn and ZnO component. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) showed that the as-synthesized product was consisted of Zn/ZnO nanocables with diameters about 50～200nm and length up to several hundreds of micrometers. TEM observation showed that both Zn and ZnO were single-crystallized and the nanocables were consisted of Zn cores and ZnO shells. There were fixed orientation relationship between the Zn cone and ZnO shell.

关 键 词：制备 纳米 产物 组成 表征 形貌 粉末 取向关系 两相 热蒸发 

分 类 号：TM248[一般工业技术—材料科学与工程]