ENHANCED RADIATION CROSSLINKING OF POLYEPICHLOROHYDRIN RUBBER

作　　者：赵文伟[1] 于黎[1] 钟晓光[1] 张月芳[1] 孙家珍[1] 

机构地区：[1]中国科学院长春应用化学研究所

出　　处：《合成橡胶工业》1994年第6期352-354,共3页China Synthetic Rubber Industry

摘　　要：在氯醚橡胶中加入７－１０份强化交联剂三丙烯酸三羟甲基的丙烷酯，置于２．７×１０＾６Ｂｑ的钴－６０辐射源中辐照，当吸收剂量为４．５×１０＾４Ｇｙ时，可制得凝胶含量为６６．４％的硫化胶，实验结果表明，在一定的吸收剂量下，凝胶含量，拉伸强度及扯断伸长率均ＴＭＰＴＡ用量的增加而增加；当吸收剂量增加时，凝胶含量，拉伸强度和扯断伸长率则下降，下降趋势随ＴＭＰＴＡ用量的增加而逐渐减弱。The irradiation behavior and the enhanced radiation crosslinking of ployepichlorohydrin rubber were studied.The results showed that the main effect of polyepichlorohydrin rubber under irradiation was the degradation resulting from the scission of ether bonds,and the enhanced crosslinking could be achieved by adding multifunctional monomers,such as trimethyol propane triacrylate.The properties of vulcanized rubber depended largely on the amount of multifunctional monomers and radiation dose.