聚晶金刚石切削齿散热电阻钎焊工艺的研究  

TECHNOLOGY OF DISSIPATION HEAT RESISTANCE BRAZING FOR POLYCRYSTALLINE DIAMOND CUTTING TEETH

作　　者：陈建民[1] 杨宝德[1] 缪青维[1] 吴志明[1] 张雷[1] 

机构地区：[1]石油大学开发系

出　　处：《石油大学学报（自然科学版）》1994年第2期64-67,共4页Journal of the University of Petroleum,China(Edition of Natural Science)

摘　　要：采用散热电阻钎焊工艺对聚晶金刚石切削齿进行钎焊，钎缝的抗剪强度达４１７．５ＭＰａ。复合片的磨耗比下降率小于１０％。采用表面测温实时监控技术，使复合片上金刚石层受热的温度低于７００℃。用复合片切削岩石，由此测定出复合片的耐磨性。这样增加了测试结果的可靠性。现场应用表明，用本工艺钎焊的聚晶金刚石切削齿制造的钻头质量稳定，基本无掉片现象。The polycrystalline diamond cutting tooth is brazed with dissipation heatresistence brazing method. The shearing strength of brazed seam is 417. 5 MPa. Reduction ofwearability of brazed polycrystalline diamond is less than 10%. The temperature ofpolycrystalline diamond is controlled under 700℃ in brazing process by means of measuringsurface temperature. The polycrystalline diamond is used to cut the rock and its wearability ismeasured. The polycrystalline diamond cutting teeth was used to make drilling bit. Field testshowed that the bit has a good reliability.

关 键 词：钎焊 聚晶金刚石 钻头 

分 类 号：TG454[金属学及工艺—焊接]