树脂NDW在苎麻棉混纺织物抗皱整理中工艺的探讨  

Process for finishing ramie/cotton blended textiles with resin NDW

作　　者：郑雪翎 

机构地区：[1]常州华源东方印染有限公司,江苏常州213003

出　　处：《印染助剂》2005年第3期43-44,共2页Textile Auxiliaries

摘　　要：对影响整理效果的树脂和催化剂用量、焙烘温度和时间等因素进行了试验,以强力损失和弹性回复角(T+W)指标为依据,找出了适合苎麻棉混纺织物抗皱整理的最佳工艺:树脂NDW100g/L、催化剂MgCl220g/L、纤维保护剂SVN20g/L,焙烘温度160℃,焙烘时间控制在3min,弹性回复角(T+W)可达265°,强力损失38.1%,DP等级达3.5级.Expts. were carried out for the factors such as resin and catalyst amts., baking temps. and time in the anti-crease finishing, and the optimum process was found for ramie blended fabrics according to the strength loss and elastic recovery angles (T+W). Elastic recovery angle (T+W) 265 °, strength loss 38.1% and DP rate 3.5 were obtained when using resin NDW 100 g/L, catalyst MgCl2 20 g/L, fiber protector SVN 20 g/L, and baking 3 min at 160 ℃.

关 键 词：混纺织物 抗皱整理 焙烘温度 强力损失 苎麻 整理效果 纤维 树脂 催化剂用量 工艺 

分 类 号：TS195[轻工技术与工程—纺织化学与染整工程] TS193[轻工技术与工程—纺织科学与工程]