Influence of welding parameters on nitrogen content in welding metal of 32Mn-7Cr-1Mo-0.3N austenitic steel  

作　　者：付瑞东 邱亮 王存宇 王青峰 郑炀曾 

机构地区：[1]Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China [2]School of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China

出　　处：《Journal of Central South University of Technology》2005年第1期22-26,共5页中南工业大学学报（英文版）

基　　金：Project(59771001) supported by the National Natural Science Foundation of China

摘　　要：The transfer behavior of nitrogen into the welding metal during gas tungsten arc welding process of 32Mn-7Cr-1Mo-0.3N steel was investigated. The effects of gas tungsten arc welding process variables, such as the volume fraction of nitrogen in shielding gas, arc holding time and arc current on the nitrogen content in the welding metal were also evaluated. The results show that the volume fraction of nitrogen in gas mixture plays a major role in controlling the nitrogen content in the welding metal. It seems that there exhibits a maximum nitrogen content (depending) on the arc current and arc holding time. The optimum volume fraction of nitrogen in shielding gas is 4% or so. The role of gas tungsten arc welding processing parameters in controlling the transfer of nitrogen is further (confirmed) by the experimental results of gas tungsten arc welding process with feeding metal.The transfer behavior of nitrogen into the welding metal during gas tungsten arc welding process of 32Mn-7Cr-1Mo-0.3N steel was investigated. The effects of gas tungsten arc welding process variables, such as the volume fraction of nitrogen in shielding gas, arc holding time and arc current on the nitrogen content in the welding metal were also evaluated. The results show that the volume fraction of nitrogen in gas mixture plays a major role in controlling the nitrogen content in the welding metal. It seems that there exhibits a maximum nitrogen content (depending) on the arc current and arc holding time. The optimum volume fraction of nitrogen in shielding gas is 4% or so. The role of gas tungsten arc welding processing parameters in controlling the transfer of nitrogen is further (confirmed) by the experimental results of gas tungsten arc welding process with feeding metal.

关 键 词：nitrogen transfer welding parameter high manganese austenitic steel DEPOSIT gas tungsten arc welding 