变形与热处理对Invar合金组织及性能的影响  

Influence of the Deformation and Heat Treatment on the Microstructures and Properties of Invar Alloy

作　　者：袁均平[1] 易丹青[1] 余志明[1] 黄正成[1] 吴伯涛[1] 张霞[1] 

机构地区：[1]中南大学材料科学与工程学院,湖南长沙410083

出　　处：《金属热处理》2005年第2期50-53,共4页Heat Treatment of Metals

摘　　要：针对实际生产中Invar合金抗跌落性能差的问题 ,对Invar合金试样进行了不同温度 (80 0℃、90 0℃、10 0 0℃ )的退火、不同变形量的冷变形及不同温度 (5 0 0℃、6 0 0℃ )的二次退火试验 ,并进行了显微组织观察和力学性能试验 ,分析各种工艺参数对Invar合金的组织和性能的影响。结果表明 ,经 80 0℃退火 + 2 3%变形 + 5 0 0℃二次退火处理的Invar合金具有最佳综合性能。Some experiments with different annealing temperature (800°C, 900°C, 1000°C), different deformation and different secondary annealing temperature (500°C, 600°C) were carried out on the invar alloy. The microstructure and mechanical properties were observed and tested respectively, and the influence of the process parameters on them was analyzed. The results show that annealed at 800°C, deformed with 23% and secondary annealed at 500°C, the invar alloy has the best comprehensive properties.

关 键 词：Invar合金 退火 二次退火 冷变形 显微组织 力学性能 

分 类 号：TG132.1[一般工业技术—材料科学与工程] TG156.21[金属学及工艺—合金]