聚苯胺全固态锂电池  

All Solid State Polyaniline Lithium Battery

作　　者：景遐斌[1] 王宝忱 彭新生[1] 冯力[1] 宋永贤[1] 

机构地区：[1]中国科学院长春应用化学研究所

出　　处：《应用化学》1994年第1期50-53,共4页Chinese Journal of Applied Chemistry

摘　　要：用经γ射线辐照交联的ＰＥＯ作为固体电解质，研究了聚苯胺（ＰＡｎ）固态锂电他的电化学特性。实验发现通过γ－辐射交联后的ＰＥＯ电解质，室温电导率可达１０（－４）Ｓ／ｃｍ以上，并具有较好的机械强度。经过６８次的充放电循环实验、电池放电容量仍维持在６０ｍＡｈ／ｇＰＡｎ以上．该电池交流阻抗分析表明，界面Ｌｉ／ＰＥＯ的阻抗远大于界面ＰＥＯ／ＰＡｎ的阻抗．循坏伏安结果显示了聚苯胺具有良好的氧化还原可逆性．The electrochemical perforrnances of all- solid state lithium battery using polyani-line positive electrode and γ-ray crosslinked PEO electrolyte containing LiClO4/PC solutionhave been studied.It showed that the ambient temperature conductivity of PEO was over10(-4)S/cm as a result of γ-ray irradiation. The capacity of over 60mAh/g and the charge- dis-charge life of over 68 cycles were achieved for the polyaniline lithium battery. The acimpedance at the Li/PEO interface was much greater than that at PEO/PAn. The result ofcyclic voltammetry showed good reversibility of the polyaniline electrode in the lithium bat-tery.

关 键 词：聚苯胺 锂电池 聚氧乙烯 辐射交联 