本钢120t转炉-LF精炼热锻用非调质钢48MnV的生产实践  

Production Practice of 120 t converter-LF Refining Microalloy Steel 48MnV for Hot forging at Benxi Iron and Steel

作　　者：张东红[1] 卢秉军[1] 

机构地区：[1]本溪钢铁(集团)特殊钢有限责任公司,本溪117001

出　　处：《特殊钢》2005年第3期59-60,共2页Special Steel

摘　　要：本钢采用铁水预处理 1 2 0t转炉吹炼 -LF精炼 4 8t铸锭 80 0轧机流程生产Φ1 50mm的热锻用非调质钢48MnV( % :0 . 42～0 . 47C ,0 .98～1 . 1 8Mn ,0 .0 6～0 . 1 0V ,0. 0 0 8～0 . 0 3 5S ,≤0 . 0 2 5P)。LF精炼时加N -Mn合金调整钢中N含量,吹氩,精炼后喂Si Ca线。经分析,钢材中氢含量( 0 . 6～1. )×1 0 - 6 ,氧含量( 8～1 5)×1 0 - 6 ,氮含量( 1 0. 8～1 4 .9)×1 0 - 6 ,轧材的力学性能为抗张强度σb81 5～880MPa ,屈服强度σs490～587MPa ,延伸率δ5 1 5%～2 1 % ,断面收缩率ψ3 2 %～44 % ,冲击值ak40～54J/cm2 ,满足标准要求。The Φ150 mm microalloy steel 48MnV (0.42～0.47C, 0.98～1.18Mn, 0.06～0.10V, 0.008～0.035S, ≤0.025P) was produced by the flow sheet: hot metal pretreatment- 120t converter blow melting- LF refining- 4.8t ingot casting- 800 mill rolling for hot forging at Benxi Steel. The nitrogen content in steel was trimmed by adding N-Mn alloy with argon stirring during LF refining, after refining feeding Si-Ca wire. The analysis results showed that hydrogen content in steel was (0.6～1)×10 -6 , oxygen content (8～15)×10 -6 and nitrogen content (108～149)×10 -6 ; The mechanical properties were tensile strength σ b 815～880 MPa, yield strength σ s 490～587 MPa, elongation δ 5 15%～21%, reduction of area ψ 32%～44%, impact value a k 40～54 J/cm 2 to meet the requirement of standard.

关 键 词：LF精炼 非调质钢 生产实践 热锻 本钢 800轧机 铁水预处理 断面收缩率 流程生产 转炉吹炼 抗张强度 力学性能 屈服强度 标准要求 N含量 氢含量 氧含量 氮含量 延伸率 冲击值 铸锭 吹氩 轧材 

分 类 号：TG316[金属学及工艺—金属压力加工]