Er:LN晶体的生长和激光性能研究  

The growth and laser properties of Mg: Er: LN crystals

作　　者：茹占军[1] 毕建聪[1] 谢家兴[1] 徐小龙[1] 

机构地区：[1]哈尔滨理工大学应用科学学院,黑龙江哈尔滨150080

出　　处：《宁波职业技术学院学报》2005年第2期90-92,共3页Journal of Ningbo Polytechnic

基　　金：国家基础研究973计划(G19990330);国家高科技发展863计划(2001AA31304)资助。

摘　　要：在LiNbO3中掺进(0、0.5、1.0、1.5mol%) Er2O3,以Czochrals技术生长LiNbO3、Er(1mol%):LiNbO3、Er(2mol%):LiNbO3、Er(3mol%):LiNbO3晶体。测试Er:LiNbO3晶体的吸收光谱,确定晶体的泵浦波长,Er:LiNbO3晶体的吸收变相对LiNbO3晶体发生红移,红移的程度随Er3+浓度的增加而增大。测试Er:LiNbO3晶体的荧光光谱,Er:LiNbO3晶体易实现激光震荡的波长4I13/2→4I15/2(～1.5μm),是制作波导激光器的最合适的波长。测试Er:LiNbO3晶体的光损伤阈值,其结果高于LiNbO3晶体。Er(3mol%):LiNbO3晶体的光损伤阈值比LiNbO3晶体高一个数量级。Doped with (0,0.5,1.0,1.5mol%) Er2O3 in LiNbO3 , following crystals were grown by the Czochralski method:LiNbO3,Er(1mol%):LiNbO3,Er(2mol%):LiNbO3 and Er(3mol%):LiNbO3. The Absorption spectra of Er:LiNbO3 crystal was measured, itspump wavelength was determined, the absorption edges of Er:LiNbO3 crystal shift to the longer wavelength in compare with thatof LiNbO3, the shifting degree increase with the heighten of Er3+ concentration. Tested the fluorescent spectra of Er:LiNbO3crystal, at the wavelength 4I13/2→4I15/2(~1.5μm) Er:LiNbO3 is prone to realize laser vibrate, which is the most suited wavelengthfor making wave-guide laser. Tested the photodamage threshold of Er:LiNbO3 crystals and find it higher than that of LiNbO3crystals. The photodamage threshold of Er(3mol%):LiNbO3 improve one order of magnitude than that of LiNbO3 crystals.

关 键 词：Er:LiNbO3晶体 激光性能 吸收光谱 

分 类 号：O734[理学—晶体学]