抑制PVC制品中小分子增塑剂迁移的研究  

Study on Anti-migration of Plasticizer with Low Molecular Weight in PVC

作　　者：张凯琳[1] 赵季若[1,2] 冯莺[1] 张学健[1] 秦齐富[1] 

机构地区：[1]青岛科技大学高分子科学与工程学院,橡塑材料与工程教育部重点实验室 [2]中国科学院长春应用化学研究所,高分子物理与化学国家重点实验室,吉林长春130022

出　　处：《中国塑料》2005年第4期62-65,共4页China Plastics

基　　金：国家自然科学基金(50373042)资助

摘　　要：采用气-固相氯化法和氯化原位接枝法对小分子增塑剂邻苯二甲酸二辛酯(DOP)进行了改性,得到的产物分别与PVC共混,并对其失重率、沸点、力学性能进行了研究。结果表明:氯含量为30%左右的氯化DOP,从PVC制品表面迁移出来的几率最小;DOP氯化原位接枝丙烯酸丁酯(BA)后作为PVC的增塑剂,当BA含量在1～10份时材料的失重较少,而BA含量在10份时材料的强度及韧性最好。The plasticizer, dioctyl phthalate(DOP),was modified through gas-solid phase chlorination and chlorinated in-situ-grafting. The migration of the modified DOP from soft poly (vinyl chloride) (PVC) was inhibited. The chlorinated DOP with a chlorine content about 30 % exhibited the lowest migration. The chlorinated DOP in-situ-grafted with butyl acrylate (BA) also gave rise to a low migration.When the amount of grafted BA was 10 phr, the plasticized PVC possessed superior strength and toughness.

关 键 词：聚氯乙烯 氯化邻苯二甲酸二辛酯 氯化原位接枝 增塑剂迁移 

分 类 号：TQ325.3[化学工程—合成树脂塑料工业]