铜离子注入不锈钢中的显微组织与抗菌性能  

Microstructure and Antibacterial Property of Stainless Steel Generated by Cu Ion Implantation

作　　者：倪红卫[1] 许伯藩[1] 熊平源[1] 但智钢[1] 熊娟[1] 

机构地区：[1]湖北省钢铁冶金重点实验室(武汉科技大学),湖北武汉430081

出　　处：《武汉科技大学学报》2005年第2期112-114,共3页Journal of Wuhan University of Science and Technology

基　　金：国家自然科学基金项目(50101009).

摘　　要：Cu离子由MEVVA离子注入机引出注入0Cr18Ni9不锈钢,采用60~100keV的能量、0.2~2.0×1017cm-2剂量。抗菌实验结果表明,铜离子注入试样具有良好的抗大肠杆菌的效果,抗菌处理使得试样具有优良的抗大肠杆菌和金黄色葡萄球菌的效果,且注入量接近饱和注入量时,样品具有最佳的抗菌性能。Copper ions were implanted into AISI 304 austenitic stainless steel (SS) by metal vapor vacuum arc (MEVVA) with 60～100 keV energy and a dose range of 0.2～5.0×10~17 cm^-2.The results show that Cu-implanted SS sample demonstrates good antibacterial property against E.coli and antibacterial treatment endows the sample with anticolibacillary and anti-staphlococcus aureus property.It is also found that,when Cu ions approach saturation,the anti-bacterial property is the best.

关 键 词：铜离子 不锈钢 抗菌性能 

分 类 号：TG142.71[一般工业技术—材料科学与工程]