65Mn钢奥氏体连续冷却转变曲线(CCT图)  

Continuous cooling transformation curve of undercooling austenite about 65Mn

作　　者：李红英[1] 耿进锋[1] 龚美涛[1] 张宇航[1] 

机构地区：[1]中南大学材料科学与工程学院,湖南长沙410083

出　　处：《材料科学与工艺》2005年第3期302-304,共3页Materials Science and Technology

摘　　要：利用膨胀法结合金相———硬度法,在Gleeble-1500热模拟机上测定了65Mn钢的临界点Ar1、Ar3、Ac1和Ac3以及Ms;测定了该钢在不同冷却速度下连续冷却时的膨胀曲线,获得了该钢的连续冷却转变曲线(CCT曲线);研究了65Mn钢连续冷却过程中奥氏体转变过程及转变产物的组织和性能,大致确定了避免网状铁素体、贝氏体以及魏氏组织铁素体的冷却速度,找出了生产65Mn钢盘条的控冷速度范围,为生产实践和新工艺的制定提供了参考依据.By dilatometric change referencing microscopic test and hardness measurement,the critical point at Ar_1,Ar_3,Ac_1and Ac_3along with Ms of 65Mn steel is determined in Gleeble-1500 thermal mechanical simulate. By measuring the different expanding curves of Continuous Cooling Transformation CCT diagram is obtained. Morphology of production with mechanical property and transformation of austenite are analysed. The cooling rates which avoide generating reticular ferrite, bainite and Widmanstaten structure ferrite are determinded.We find the range of proper control-cooling rate about 65Mn rolled steel wire.All those provid the references for productive practice and establishing new technics.

关 键 词：连续冷却转变曲线 65MN钢 奥氏体 CCT图 冷却速度 CCT曲线 组织和性能 网状铁素体 热模拟机 膨胀曲线 转变过程 冷却过程 魏氏组织 生产实践 硬度法 合金相 膨胀法 临界点 Ac1 贝氏体 钢盘条 测定 控冷 

分 类 号：TG142.33[一般工业技术—材料科学与工程] TG161[金属学及工艺—金属材料]