脱硫醇尾气渗铝管线焊缝腐蚀开裂原因分析  

Analysis of Causes of Corrosion Cracking of Welds of Al-diffused Tail Gas Pipelines in De-mercaptan Service

作　　者：李选亭[1] 

机构地区：[1]洛阳石油化工工程公司工程研究院,河南洛阳471003

出　　处：《石油化工腐蚀与防护》2005年第3期50-52,共3页Corrosion & Protection In Petrochemical Industry

摘　　要：对洛阳石油化工总厂脱硫醇尾气渗铝管线焊缝腐蚀开裂及近焊缝处渗铝钢腐蚀的原因进行了分析,指出主要是焊接质量问题所致,而在脱硫醇尾气所含的腐蚀介质中S,Cl,N等元素加速了焊缝及近焊缝处渗铝钢腐蚀开裂,通过控制焊缝质量可使腐蚀得到控制。The corrosion cracking of welds of tail gas Al-diffused pipelines and the corrosion of Al-diffused steel near the welds in the de-mer-captan service of Luoyang Petrochemical Complex are analyzed. The analysis concludes that the corrosion cracking is caused by the poor welding quality and accelerated by S, C1 and N etc in the corrosive media. The corrosion cracking can be controlled by controlling the welding quality of welds.

关 键 词：脱硫醇 渗铝管 焊缝腐蚀开裂 焊接 

分 类 号：TG172.2[金属学及工艺—金属表面处理]