TiC/耐热钢钢结硬质合金原位反应合成研究  

A study on in situ reactive synthesis of TiC/heat resistant steel-steel bonded carbides

作　　者：刘均海[1] 黄继华[1] 宋桂香[1] 张建纲[1] 

机构地区：[1]北京科技大学材料科学与工程学院,北京100083

出　　处：《粉末冶金技术》2005年第3期199-203,共5页Powder Metallurgy Technology

摘　　要：以钛铁粉、铬铁粉、铁粉、胶体石墨等为原料,原位反应合成了TiC/耐热钢钢结硬质合金,并用扫描电镜(SEM)、X射线衍射等测试方法对所制备的试样进行了组织结构分析。研究结果表明:反应合成的钢结硬质合金主要相组成为TiC+FeCr固熔体,所合成的硬质相TiC颗粒细小,随烧结温度升高TiC颗粒略有长大。当加入一定的钼与硼后,钢结硬质合金硬度和致密度提高,TiC颗粒尺寸减小,分布更均匀。TiC_p/Heat resistant steel-steel bonded carbides were in situ synthesized by sintering compacts of mixed ferrotianium, ferrochromium, iron,carbon powders. The microstructure of the steel bonded carbides was analyzed by scanning electron microscope (SEM) and X-ray diffraction(XRD). The results show that the synthesized steel bonded carbides consist of fine TiC particles and a Fe-Cr solid solution as the binder phase. The size of TiC particles increases with the increase of the sintering temperature. The addition of molybdenum and boron is beneficial to the densification of the steel bonded carbides, the refinement and the distribution uniformity of the TiC particles.

关 键 词：钢结硬质合金 合成研究 扫描电镜(SEM) TIC颗粒 原位反应合成 组织结构分析 X射线衍射 胶体石墨 测试方法 研究结果 温度升高 颗粒尺寸 钛铁粉 耐热钢 固熔体 相组成 硬质相 致密度 烧结 

分 类 号：TF125.32[冶金工程—粉末冶金] TQ612.9[冶金工程—冶金物理化学]